物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.19 g/cc | 1.19 g/cc | DAM; ASTM D792 |
密度 | 1.19 g/cc | 0.0430 lb/in³ | DAM; ISO 1183 |
填料含量 | 14 % | 14 % | DAM |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
洛氏硬度(M 级) | 70 | 70 | DAM; ISO 2039/2 |
洛氏硬度(R 级) | 110 | 110 | DAM; ISO 2039/2 |
抗张强度(断裂) |
85.0 MPa
@Temperature 23.0 °C |
12300 psi
@Temperature 73.4 °F |
DAM; ISO 527 |
抗张强度 |
90.0 MPa
@Temperature 23.0 °C |
13100 psi
@Temperature 73.4 °F |
DAM; ASTM D638 |
伸长率 (断裂) |
6.0 %
@Temperature 23.0 °C |
6.0 %
@Temperature 73.4 °F |
DAM; ASTM D638 |
|
9.0 %
@Temperature 23.0 °C |
9.0 %
@Temperature 73.4 °F |
DAM; ISO 527 |
拉伸模量 |
4.20 GPa
@Temperature 23.0 °C |
609 ksi
@Temperature 73.4 °F |
DAM; ISO 527 |
弯曲模量 |
3.60 GPa
@Temperature 23.0 °C |
522 ksi
@Temperature 73.4 °F |
DAM; ISO 178 |
|
3.66 GPa
@Temperature 23.0 °C |
531 ksi
@Temperature 73.4 °F |
DAM; ASTM D790 |
悬壁梁缺口冲击强度 |
1.40 J/cm
@Temperature 23.0 °C |
2.62 ft-lb/in
@Temperature 73.4 °F |
DAM; ASTM D256 |
悬壁梁无缺口冲击强度 |
9.60 J/cm
@Temperature 23.0 °C |
18.0 ft-lb/in
@Temperature 73.4 °F |
DAM; ASTM D4812 |
悬壁梁缺口冲击强度 |
7.00 kJ/m²
@Temperature -40.0 °C |
3.33 ft-lb/in²
@Temperature -40.0 °F |
DAM; ISO 180/1A |
|
13.0 kJ/m²
@Temperature 23.0 °C |
6.19 ft-lb/in²
@Temperature 73.4 °F |
DAM; ISO 180/1A |
简支梁缺口冲击强度 |
0.400 J/cm²
@Temperature -40.0 °C |
1.90 ft-lb/in²
@Temperature -40.0 °F |
DAM; ISO 179/1eA |
|
1.20 J/cm²
@Temperature 23.0 °C |
5.71 ft-lb/in²
@Temperature 73.4 °F |
DAM; ISO 179/1eA |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
相比耐漏电起痕指数(CTI) |
580 V
@Temperature 23.0 °C |
580 V
@Temperature 73.4 °F |
DAM; UL 746A |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线形热膨胀系数 - 流动 |
500 µm/m-°C
@Temperature -40.0 - 23.0 °C |
278 µin/in-°F
@Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 |
|
500 µm/m-°C
@Temperature 23.0 - 55.0 °C |
278 µin/in-°F
@Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
|
500 µm/m-°C
@Temperature 55.0 - 160 °C |
278 µin/in-°F
@Temperature 131 - 320 °F |
DAM; ASTM E 831 |
|
500 µm/m-°C
@Temperature -40.0 - 23.0 °C |
278 µin/in-°F
@Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
|
500 µm/m-°C
@Temperature 23.0 - 55.0 °C |
278 µin/in-°F
@Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
|
500 µm/m-°C
@Temperature 55.0 - 160 °C |
278 µin/in-°F
@Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 |
线性热膨胀系数,横向流动 |
96.0 µm/m-°C
@Temperature -40.0 - 23.0 °C |
53.3 µin/in-°F
@Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 |
|
96.0 µm/m-°C
@Temperature -40.0 - 23.0 °C |
53.3 µin/in-°F
@Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
|
118 µm/m-°C
@Temperature 23.0 - 55.0 °C |
65.6 µin/in-°F
@Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
|
118 µm/m-°C
@Temperature 23.0 - 55.0 °C |
65.6 µin/in-°F
@Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
|
123 µm/m-°C
@Temperature 55.0 - 160 °C |
68.3 µin/in-°F
@Temperature 131 - 320 °F |
DAM; ASTM E 831 |
|
123 µm/m-°C
@Temperature 55.0 - 160 °C |
68.3 µin/in-°F
@Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 |
熔融温度 | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
|
263 °C | 505 °F | DAM; ASTM D3418 |
载荷下热变形温度(0.46 MPa) | 246 °C | 475 °F | DAM; ISO 75-1/-2 |
载荷下热变形温度(1.8 MPa) | 195 °C | 383 °F | DAM; ISO 75-1/-2 |
|
205 °C | 401 °F | DAM; ASTM D648 |
UL RTI |
120 °C
@Thickness 3.00 mm |
248 °F
@Thickness 0.118 in |
DAM; UL 746B |
|
120 °C
@Thickness 1.50 mm |
248 °F
@Thickness 0.0591 in |
DAM; UL 746B |
|
120 °C
@Thickness 0.750 mm |
248 °F
@Thickness 0.0295 in |
DAM; UL 746B |
UL RTI,机械冲击 |
65.0 °C
@Thickness 0.750 mm |
149 °F
@Thickness 0.0295 in |
DAM; UL 746B |
|
95.0 °C
@Thickness 1.50 mm |
203 °F
@Thickness 0.0591 in |
DAM; UL 746B |
|
105 °C
@Thickness 3.00 mm |
221 °F
@Thickness 0.118 in |
DAM; UL 746B |
UL RTI,机械无冲击 |
85.0 °C
@Thickness 0.750 mm |
185 °F
@Thickness 0.0295 in |
DAM; UL 746B |
|
105 °C
@Thickness 1.50 mm |
221 °F
@Thickness 0.0591 in |
DAM; UL 746B |
|
105 °C
@Thickness 3.00 mm |
221 °F
@Thickness 0.118 in |
DAM; UL 746B |
可燃性(UL94) |
HB
@Thickness 0.750 mm |
HB
@Thickness 0.0295 in |
DAM; IEC 60695-11-10 |
|
HB
@Thickness 1.50 mm |
HB
@Thickness 0.0591 in |
DAM; IEC 60695-11-10 |
|
HB
@Thickness 3.00 mm |
HB
@Thickness 0.118 in |
DAM; IEC 60695-11-10 |
|
HB
@Thickness 3.00 mm |
HB
@Thickness 0.118 in |
DAM; UL94 |
|
HB
@Thickness 1.50 mm |
HB
@Thickness 0.0591 in |
DAM; UL94 |
|
HB
@Thickness 0.750 mm |
HB
@Thickness 0.0295 in |
DAM; UL94 |
加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
加工(熔体)温度 | 295 °C | 563 °F | DAM; Optimum |
|
285 - 305 °C | 545 - 581 °F | DAM |
模具温度 | 50.0 - 100 °C | 122 - 212 °F | DAM |
|
80.0 °C | 176 °F | DAM; optimum |
干燥温度 | 80.0 °C | 176 °F | DAM |
干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
水分含量 | <= 0.20 % | <= 0.20 % | DAM |
材料描述 |
|
测试方法 |
---|---|---|
添加剂 | Heat Stabilizer | DAM |
外观 | Black Color | DAM |
|
Colors Available | DAM |
Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
特性 | Impact Resistance, High | DAM |
|
Toughness, Good | DAM |
Filler | Glass fiber reinforcement | DAM |
形式 | Pellets | DAM |
Generic | Nylon 66 | DAM |
Heat Stabilized | Yes | DAM |
Material Status | Current | DAM |
部件标识代码 | >PA66-IGF14< | ISO 11469; DAM |
Polymer Family | Polyamide | DAM |
Polymer Type | PA66 | DAM |
加工方法 | Injection Molding | DAM |
产品分类 | Glass Reinforced Resins | DAM |
|
Toughened Resins | DAM |
树脂识别 | PA66-IGF14 | ISO 1043; DAM |
符合RoHS指令 | Contact Manufacturer | DAM |
Ultrasonic Weldable | Yes | DAM |
用途 | Appliance Components | DAM |
|
Automotive Applications | DAM |
|
Fasteners | DAM |
|
Industrial Applications | DAM |
|
Sporting Goods | DAM |
- 公司类型私营有限责任公司
- 经营模式经销商-私营有限责任公司
- 联系人张涛
- 联系手机13662912617
- 联系固话0755-87898878
- 公司地址广东省深圳市龙华区大浪街道高峰社区长燊大厦3层
-
PA66 209 TFE 5 美国RTP原料提供 ¥10.00
-
PA66 109-14 G 美国Teknor Apex加工材料增强 ¥10.00
-
PA66 IM5 BK 美国TPC生产应用卖 ¥10.00
-
PA66 GF 45 斯洛伐克Plastcom化工材料提供 ¥10.00
-
PA66 6 5021 T 欧洲宇部品牌化工塑胶粒 ¥10.00
-
PA66 6 C2 ZV30 法国Addiplast加工材料有售 ¥10.00
-
PA66 6 AB700 UF 美国普立万化工材料提供 ¥10.00
-
PA66 ZR01 平顶山海瑞祥产品应用现货 ¥10.00
-
PA66 EMI 281 美国RTP生产应用专卖 ¥10.00
-
PA66 LD950 韩国现代工厂应用有售 ¥10.00
-
PA66 6 C2 法国Addiplast生产应用卖 ¥10.00
-
PA66 26001 NA LF 美国福禄化工材料原厂 ¥10.00
-
美国杜邦PA66 代理商 ¥20.00
-
德国巴斯夫PA66代理 ¥20.00
-
PA66 6 C3 HU natur 德国Akro-Plastic工厂应用原厂 ¥10.00