DuPont Zybbb? 8018HS NC010 Nylon 66(聚酰胺-尼龙66)
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Specific Gravity比重
1.19g/cc
1.19g/cc
DAM; ASTM D792
Filler Content填料含量
14 %
14 %
DAM
Water Absorption吸水率
1.9 %@Thickness 1.00 mm,Temperature 23.0 °C
1.9 %@Thickness 0.0394 in,Temperature 73.4 °F
Equilibrium 50%RH; DAM; ISO 62, Similar to
6.3 %@Thickness 1.00 mm,Temperature 23.0 °C
6.3 %@Thickness 0.0394 in,Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow线性收缩率/流动
0.0080cm/cm@Thickness 2.00 mm
0.0080in/in@Thickness 0.0787 in
Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse线性收缩率/横向
0.0070cm/cm@Thickness 2.00 mm
0.0070in/in@Thickness 0.0787 in
Normal; DAM; ISO 294-4
Mechanical Properties力学性能
Metric公制数据
English英制数据
Comments测试方法
Tensile Strength at Break断裂拉伸强度
58.0MPa@Temperature 23.0 °C
8410psi@Temperature 73.4 °F
50%RH; ISO 527
85.0MPa@Temperature 23.0 °C
12300psi@Temperature 73.4 °F
DAM; ISO 527
Tensile Strength拉伸强度
60.0MPa@Temperature 23.0 °C
8700psi@Temperature 73.4 °F
50%RH; ASTM D638
90.0MPa@Temperature 23.0 °C
13100psi@Temperature 73.4 °F
DAM; ASTM D638
Tensile Stress拉伸应力
0.000MPa@Strain 0.000 %,Temperature 23.0 °C
0.000psi@Strain 0.000 %,Temperature 73.4 °F
DAM; ISO 527
9.60MPa@Strain 0.600 %,Temperature 80.0 °C
1390psi@Strain 0.600 %,Temperature 176 °F
DAM; ISO 527
49.5MPa@Strain 8.50 %,Temperature 80.0 °C
7180psi@Strain 8.50 %,Temperature 176 °F
DAM; ISO 527
68.602MPa@Strain 2.10 %,Temperature 23.0 °C
9949.9psi@Strain 2.10 %,Temperature 73.4 °F
DAM; ISO 527
79.288MPa@Strain 2.90 %,Temperature 23.0 °C
11500psi@Strain 2.90 %,Temperature 73.4 °F
DAM; ISO 527
DuPont Zybbb? 8018HS NC010 Nylon 66(聚酰胺-尼龙66)
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
Specific Gravity比重
|
1.19g/cc
|
1.19g/cc
|
DAM; ASTM D792
|
Filler Content填料含量
|
14 %
|
14 %
|
DAM
|
Water Absorption吸水率
|
1.9 %@Thickness 1.00 mm,Temperature 23.0 °C
|
1.9 %@Thickness 0.0394 in,Temperature 73.4 °F
|
Equilibrium 50%RH; DAM; ISO 62, Similar to
|
6.3 %@Thickness 1.00 mm,Temperature 23.0 °C
|
6.3 %@Thickness 0.0394 in,Temperature 73.4 °F
|
Saturation, immersed; DAM; ISO 62, Similar to
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.0080cm/cm@Thickness 2.00 mm
|
0.0080in/in@Thickness 0.0787 in
|
Parallel; DAM; ISO 294-4
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.0070cm/cm@Thickness 2.00 mm
|
0.0070in/in@Thickness 0.0787 in
|
Normal; DAM; ISO 294-4
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
Tensile Strength at Break断裂拉伸强度
|
58.0MPa@Temperature 23.0 °C
|
8410psi@Temperature 73.4 °F
|
50%RH; ISO 527
|
85.0MPa@Temperature 23.0 °C
|
12300psi@Temperature 73.4 °F
|
DAM; ISO 527
|
|
Tensile Strength拉伸强度
|
60.0MPa@Temperature 23.0 °C
|
8700psi@Temperature 73.4 °F
|
50%RH; ASTM D638
|
90.0MPa@Temperature 23.0 °C
|
13100psi@Temperature 73.4 °F
|
DAM; ASTM D638
|
|
Tensile Stress拉伸应力
|
0.000MPa@Strain 0.000 %,Temperature 23.0 °C
|
0.000psi@Strain 0.000 %,Temperature 73.4 °F
|
DAM; ISO 527
|
9.60MPa@Strain 0.600 %,Temperature 80.0 °C
|
1390psi@Strain 0.600 %,Temperature 176 °F
|
DAM; ISO 527
|
|
49.5MPa@Strain 8.50 %,Temperature 80.0 °C
|
7180psi@Strain 8.50 %,Temperature 176 °F
|
DAM; ISO 527
|
|
68.602MPa@Strain 2.10 %,Temperature 23.0 °C
|
9949.9psi@Strain 2.10 %,Temperature 73.4 °F
|
DAM; ISO 527
|
|
79.288MPa@Strain 2.90 %,Temperature 23.0 °C
|
11500psi@Strain 2.90 %,Temperature 73.4 °F
|
DAM; ISO 527
|
PA66美国杜邦 8018 14%玻纤增强
PA66美国杜邦8018塑胶原料为半透明或不透明乳白色结晶形聚合物,具有可塑性。密度1.19g/cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。 连续耐热80-120℃,平衡吸水率2.5%。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀,但易容于苯酚、甲酸等极性溶剂。具有优良的 性、自润滑性,机械强度较高。但吸水性较大,因而尺寸稳定性较差
PA66是PA系列中机械强度、应用 的品种,因其结晶度高,故其刚性、耐热性都较高。
PA66美国杜邦8018用于高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等
PA66性质:结晶性热可塑性塑料,有明显熔点,Nylon6Tm为220-230℃,Nylon66则为260-270℃,
Nylon本身具吸水基故有吸水性,成形前须干燥,温度过高干燥则尼龙粒变色。
优点:1、具高抗张强度;2、耐韧、耐冲击性特优;3、自润性 性佳、耐 性优;4、低温特性佳;5、具自熄性;
用途:广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车:散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类:防静电PA,导电PA,加纤防火PA,防火PA,抗紫外线耐候PA,高温挤出级PA。
导电尼龙66:具有良好的 性、耐热性、耐油性及耐化学 性,还大大降低了原材料的吸水率和收缩率,
具有优良的尺寸稳定性及优异的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制,
适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围,可用于注塑及挤出等成型。
有很多*金属和涂装的优点:零件重量较轻,较易处理,运输成本较低。它们的装配简便,制造成本较低,并且较不会受到撞凹,割损和刮伤。
为了标识或美观目的,一些材料可被预先染色,避 时且昂贵的两次着色加工
- 公司类型私营有限责任公司
- 经营模式经销商-私营有限责任公司
- 联系人张涛
- 联系手机13662912617
- 联系固话0755-87898878
- 公司地址广东省深圳市龙华区大浪街道高峰社区长燊大厦3层
-
PA66 209 TFE 5 美国RTP原料提供 ¥10.00
-
PA66 109-14 G 美国Teknor Apex加工材料增强 ¥10.00
-
PA66 IM5 BK 美国TPC生产应用卖 ¥10.00
-
PA66 GF 45 斯洛伐克Plastcom化工材料提供 ¥10.00
-
PA66 6 5021 T 欧洲宇部品牌化工塑胶粒 ¥10.00
-
PA66 6 C2 ZV30 法国Addiplast加工材料有售 ¥10.00
-
PA66 6 AB700 UF 美国普立万化工材料提供 ¥10.00
-
PA66 ZR01 平顶山海瑞祥产品应用现货 ¥10.00
-
PA66 EMI 281 美国RTP生产应用专卖 ¥10.00
-
PA66 LD950 韩国现代工厂应用有售 ¥10.00
-
PA66 6 C2 法国Addiplast生产应用卖 ¥10.00
-
PA66 26001 NA LF 美国福禄化工材料原厂 ¥10.00
-
美国杜邦PA66 代理商 ¥20.00
-
德国巴斯夫PA66代理 ¥20.00
-
PA66 6 C3 HU natur 德国Akro-Plastic工厂应用原厂 ¥10.00